CW612N Forging Brass

CW612N Forging Brass Specification

Usage
Automotive, Builders Hardware, Consumer Fasteners, Industrial Plumbing

Tolerance
1.5 to 125 Millimeter (mm)

Surface Finishing
Bright

Processing Type
Extruded & Drawn

Color
Golden

Finish
Extruded & Drawn

Product Type
Architecture, Builders Hardware

Application
Automotive, Builders Hardware, Consumer Fasteners, Industrial Plumbing

Dimension (L*W*H)
16 Foot (ft)

Material
Brass

Size
1.5mm to 125mm

Grade
CW612N

Alloy
Yes

Temper
1/2 Hard

Length
16 Foot (ft)

Shape
Round

Diameter
1.5 Millimeter (mm)

Warranty
NA

CW612N Forging Brass Trade Information

Minimum Order Quantity
2000 Kilograms

Delivery Time
4 Week

About CW612N Forging Brass

Brass is an alloy mainly consisting of copper and zinc. Brass alloys can be easily shaped and are available in various colors. Brass has high thermal conductivity. CW612N forging brass alloys have good forgeability. They are available in the form of rod.

The following datasheet gives details about CW612N brass alloys.

Chemical Composition

Elements	Min (%)	Max (%)
Cu	59.00	60.00
Pb	1.60	2.50
Sn	-	0.30
Fe	-	0.30
Al	-	0.05
Ni	-	0.30
Total Others	-	0.20
Zn	Remainder

Mechanical Properties according To EN12164 (As Per Temper R410)

Range (mm)	From	To	UTS Min (N/mm)	PS Min (N/mm)	Elongation Min (%)	Hardness Min	Hardness Max
Round (Da)	2	40	410	230	12	-	-
Hex (A/F)	2	35	410	230	12	-	-
Square (A/F)	2	35	410	230	12	-	-

Physical Properties

Melting Point Liquidus F	1640
Melting Point Solidus F	1620
Density lb/cu in. at 68F	0.305
Specific Gravity	8.44
Electrical Conductivity % IACS at 68F	27
Thermal Conductivity Btu/ sq ft/ ft hr/ F at 68F	69
Coefficient of Thermal Expansion 68-57210 per F (68 572F)	11.5
Specific Heat Capacity Btu/ lb /F at 68F	0.09
Modulus of Elasticity in Tension ksi	15000
Modulus of Rigidity ksi	5600

Fabrication Properties

Technique	Suitability
Soldering	Excellent
Brazing	Good
Oxyacetylene Welding	Not Recommended
Gas Shielded Arc Welding	Not Recommended
Coated Metal Arc Welding	Not Recommended
Spot Weld	Not Recommended
Seam Weld	Not Recommended
Butt Weld	Fair
Capacity for Being Cold Worked	Poor
Capacity for Being Hot Formed	Excellent
Forgeability Rating	100
Machinability Rating	80