C36500 Forging Brass

C36500 Forging Brass Specification

Usage
Automotive, Builders Hardware, Consumer Fasteners, Industrial Plumbing

Size
1.5mm to 125mm

Processing Type
Extruded & Drawn

Product Type
Architecture, Builders Hardware

Material
Brass

Dimension (L*W*H)
16 Foot (ft)

Finish
Extruded & Drawn

Surface Finishing
Bright

Application
Automotive, Builders Hardware, Consumer Fasteners, Industrial Plumbing

Tolerance
1.5 to 125 Millimeter (mm)

Color
Golden

Grade
C36500

Alloy
Yes

Temper
1/2 Hard

Length
16 Foot (ft)

Shape
Round

Diameter
1.5 Millimeter (mm)

Warranty
NA

C36500 Forging Brass Trade Information

Minimum Order Quantity
2000 Kilograms

Delivery Time
4 Week

About C36500 Forging Brass

C36500 are the standard materials for machining (machining index 100 %). These alloys are also particularly suitable for hot stamping when the forged parts are subsequently machined extensively. Is recommended for applications where cold working with little reduction such as knurling is used. The ductility of this material makes it particularly suitable for the manufacture of wires as well as rods and sections.

Chemical Composition

Elements	Min (%)	Max (%)
Cu	58.00	61.00
Pb	0.25	0.70
Fe	-	0.15
Total Others	-	0.40
Zn	Remainder

Mechanical Properties According To ASTM B981 (As Per Temper HO2)

Range (Inch)	From	To	UTS Min (ksi)	PS Min (ksi)	Elongation Min (%)	Hardness Min	Hardness Max (HRB)
Round (Dia)	0.059	0.500	53	28	10	-	-
0.500	1.000	55	26	12	-	-
1.000	2.000	48	24	20	-	-
2.000	2.953	45	20	25	-	-
Hex (A/F)	0.118	0.500	53	28	10	-	-
0.500	1.000	55	26	12	-	-
1.000	2.000	48	24	20	-	-
2.000	2.756	45	20	25	-	-
Square (A/F)	0.118	0.500	53	28	10	-	-
0.500	1.000	55	26	12	-	-
1.000	2.000	48	24	20	-	-
2.000	2.362	45	20	25	-	-
Octagon (A/F)	0.118	0.500	53	28	10	-	-
0.500	1.000	55	26	12	-	-
1.000	2.000	48	24	20	-	-
2.000	2.362	45	20	25	-	-
Rectangle (Thickness)	0.118	0.500	53	28	10	-	-
0.500	1.000	55	26	12	-	-
1.000	2.000	48	24	20	-	-

Range (mm)	From	To	UTS Min (MPa)	PS Min (MPa)	Elongation Min (%)	Hardness Min	Hardness Max
Round (Dia)	1.5	12	430	390	10	-	-
12	25	380	180	12	-	-
25	50	330	165	20	-	-
50	75	310	135	25	-	-
Hex (A/F)	1.5	12	430	390	10	-	-
12	25	380	180	12	-	-
25	50	330	165	20	-	-
50	70	310	135	25	-	-
Square (A/F)	1.5	12	430	390	10	-	-
12	25	380	180	12	-	-
25	50	330	165	20	-	-
50	60	310	135	25	-	-
Octagon (A/F)	1.5	12	430	390	10	-	-
12	25	380	180	12	-	-
25	50	330	165	20	-	-
50	60	310	135	25	-	-
Rectangle (Thickness)	3	12	430	390	10	-	-
12	25	380	180	12	-	-
25	50	330	165	20	-	-

Physical Properties

Melting Point Liquidus F	1650
Melting Point Solidus F	1630
Density lb/cu in. at 68F	0.304
Specific Gravity	8.41
Electrical Conductivity% IACS at 68F	28
Thermal Conductivity Btu/ sq ft/ ft hr/ F at 68F	71
Coefficient of Thermal Expansion 68-57210 per F (68 572F)	11.6
Specific Heat Capacity Btu/ lb /F at 68F	0.09
Modulus of Elasticity in Tension ksi	15000
Modulus of Rigidity ksi	5600

Technique	Suitability
Soldering	Excellent
Brazing	Good
Oxyacetylene Welding	Fair
Gas Shielded Arc Welding	Fair
Coated Metal Arc Welding	Not Recommended
Spot Weld	Not Recommended
Seam Weld	Not Recommended
Butt Weld	Fair
Capacity for Being Cold Worked	Fair
Capacity for Being Hot Formed	Excellent
Machinability Rating	60