C3604 Free Machining Brass

C3604 Free Machining Brass Specification

Surface Finishing
Bright

Size
1.5mm to 125mm

Finish
Extruded & Drawn

Color
Golden

Material
Brass

Tolerance
1.5 to 125 Millimeter (mm)

Usage
Automotive, Builders Hardware, Consumer Fasteners, Industrial Plumbing

Dimension (L*W*H)
16 Foot (ft)

Product Type
Bars, Rods, Billets, Coils, Hollows, Ingots

Processing Type
Extruded & Drawn

Application
Automotive, Builders Hardware, Consumer Fasteners, Industrial Plumbing

Grade
C3604

Alloy
Yes

Temper
1/2 Hard

Length
16 Foot (ft)

Shape
Round

Diameter
1.5 Millimeter (mm)

Warranty
NA

C3604 Free Machining Brass Trade Information

Minimum Order Quantity
2000 Kilograms

Delivery Time
4 Week

About C3604 Free Machining Brass

C3604, Free cutting brass, is a significantly improved form of 60/40 brass, with excellent free cutting properties. It is used in the mass production of brass components where maximum output and longest tool life are required, and where no further cold forming after machining is required.

Chemical Composition

Elements	Min (%)	Max (%)
Cu	57.00	61.00
Pb	1.80	3.70
Fe	-	0.50
Sn + Fe	-	1.20
Zn	Remainder

Mechanical Properties According To H3250 JIS C3604 (As Per Temper BD)

Range (mm)	From	To	UTS Min (N/mm)	PS Min	Elongation Min (%)	Hardness Min (HV)	Hardness Max
Round (Dia)	1.5	75	335	-	-	80	-
Hex (A/F)	3	70	335	-	-	80	-
Square (A/F)	3	60	335	-	-	80	-
Rectangle (Thickness)	3	50	335	-	-	80	-

Physical Properties

Melting Point Liquidus F	1630
Melting Point Solidus F	1610
Density lb/cu in. at 68F	0.306
Specific Gravity	8.47
Electrical Conductivity% IACS at 68F	28
Thermal Conductivity Btu/ sq ft/ ft hr/ F at 68F	71
Coefficient of Thermal Expansion 68-57210 per F (68 572F)	11.6
Specific Heat Capacity Btu/ lb /F at 68F	0.09
Modulus of Elasticity in Tension ksi	14000
Modulus of Rigidity ksi	5300

Fabrication Properties

Technique	Suitability
Soldering	Excellent
Brazing	Good
Oxyacetylene Welding	Not Recommended
Gas Shielded Arc Welding	Not Recommended
Coated Metal Arc Welding	Not Recommended
Spot Weld	Not Recommended
Seam Weld	Not Recommended
Butt Weld	Fair
Capacity for Being Cold Worked	Poor
Capacity for Being Hot Formed	Excellent
Machinability Rating	90